Precast Block Characteristics:1.Simple structure and easy to install.
2.Good integrity and impermeability.
3.Longer working life than the traditional one.
4.Energy-saving and environment-friendly.
Precast Block Application:The pre-cast refractory block is mainly used for the coke oven.
Precast Block Technical Data Sheet:
Item |
Pre-cast Coke Door |
ω Al2O3 (%) |
≥50 |
ω MgO (%) |
≥3 |
Apparent Porosity (%) |
≤28 |
Bulk Density (g/cm3) |
≥2.1 |
Cold Crushing Strength (MPa) |
≥35 |
Rupture Strength (MPa) |
≥4 |
Thermal Conductivity at 1000℃ (Heating Side) [w/(m·k)] |
≤1.2 |
Thermal Shock Resistance (1100℃, water cooling) (cycle) |
≥ 50 |
Item |
Glazed Coal-charging Hole & Bell Pre-cast Refractory |
ω Al2O3 (%) |
≥45 |
ω MgO (%) |
≥2.5 |
Apparent Porosity (%) |
≤28 |
Bulk Density (g/cm3) |
≥2.1 |
Cold Crushing Strength (MPa) |
≥40 |
Rupture Strength (MPa) |
≥4 |
Thermal Conductivity at 1000℃ (Heating Side) [W/(m·K] |
≤1.2 |
Thermal Shock Resistance (1100℃, water cooling) (cycle) |
≥50 |
Item |
Normal Coal-charging Hole & Bell Pre-cast Refractory |
ω Al2O3 (%) |
≥45 |
ω MgO (%) |
≥2.5 |
Apparent Porosity (%) |
≤28 |
Bulk Density (g/cm3) |
≥2.1 |
Cold Crushing Strength (MPa) |
110℃*24h After drying |
≥35 |
1350℃*3h After firing |
≥40 |
Rupture Strength (MPa) |
110℃*24h After drying |
≥3 |
1350℃*3h After firing |
≥4 |
Thermal Conductivity at 1000℃ (Heating Side) [w/(m·k)] |
≤1.2 |
Thermal Shock Resistance (1100℃, water cooling) (cycle) |
≥50 |
Item |
Glazed Ascending Pipe Pre-cast Refractory |
ω Al2O3 (%) |
≥50 |
ω MgO (%) |
≥2.5 |
Apparent Porosity (%) |
≤28 |
Bulk Density (g/cm3) |
≥2.1 |
Cold Crushing Strength (MPa) |
≥40 |
Rupture Strength (MPa) |
≥4 |
Thermal Conductivity at 1000℃ (Heating Side) [W/ (m·K)] |
≤1.2 |
Thermal Shock Resistance (1100℃, water cooling) (cycle) |
≥50 |
Item |
Normal Ascending Pipe Pre-cast Refractory |
ω Al2O3 (%) |
≥50 |
ω MgO (%) |
≥2.5 |
Apparent Porosity (%) |
≤28 |
Bulk Density (g/cm3) |
≥2.1 |
Cold Crushing Strength (MPa) |
110℃*24h After drying |
≥35 |
1350℃*3h After firing |
≥40 |
Rupture Strength (MPa) |
110℃*24h After drying |
≥3.5 |
1350℃*3h After firing |
≥4 |
Thermal Conductivity at 1000℃ (Heating Side) [w/(m·k)] |
≤1.2 |
Thermal Shock Resistance (1100℃, water cooling) (cycle) |
≥50 |