Item | KA40-1 | KA40-1 | Test Standard | |
Al2O3 (%) | μG | ≥40 | ≥35 | DIN51070 3 part |
δ | 1.5 | 1.5 | ||
Fe2O3 (%) | μG | ≤2.0 | ≤2.0 | DIN501070/5 |
δ | 0.5 | 0.5 | ||
Apparent Porosity (%) | μG | ≤20 | ≤24 | DIN501056 |
δ | 2 | 2 | ||
Cold Crushing Strength (MPa) (KDF) | μG | ≥35 | ≥30 | DIN51067/1 |
δ | 10 | 10 | ||
Xmin | 25 | 20 | ||
Refractoriness under Load (DFB) ta ℃ | μG | ≥1450 | ≥1400 | DIN51064 |
δ | 40 | 40 | ||
Refractoriness under Load (DFB) ta ℃ | μG | ≥1350 | ≥1300 | DIN51053/1 |
δ | 25 | 25 | ||
Refractoriness (DEL) (℃) | μG | ≥172/174 (SK33) | DIN51063/1 | |
δ | 2 (SK1) |