Items | Al(H2PO4)3 Combined | H2PO4 Combined | ||
GPL75 | GPL60 | GPL75 | ||
Al2O3 (%) | ≥75 | ≥60 | ≥75 | |
Bulk Density (g/m3) | ≥2.60 | ≥2.23 | ≥2.70 | |
Compression Strength (MPa) | 110℃x24h | 34.9 | 28.1 | 32.5 |
1000℃x3h | 28.6 | 26.3 | 37.0 | |
1200℃x3h | 46.5 | 35.4 | 48.0 | |
1400℃x3h | 41.3 | 30.4 | 39.0 | |
Thermal Compressive Strength (MPa) |
1000℃x3h | 29.2 | 30.8 | 33.0 |
1200℃x1h | 8.5 | 9.0 | 11.0 | |
Permanent Linear Change (%) | 1400℃x3h | 0-0.65 | 0-0.92 | 0-1.07 |
Refractoriness Under Load at 0.20Mpa (℃) | Distortion 0.6% | 1250 | 1190 | 1310 |
Distortion 4% | 1455 | 1470 | 1480 | |
Thermal Shock Resistance (cycle) | 800℃, water cooling | ≥50 | ≥50 | ≥50 |