Item | Unit | Fire Clay Insulation Brick | |||
Brand | FNG-0.8 | FNG-1.0 | FNG-1.3 | ||
Chemical Composition | Al2O3 | % | ≥15 | ≥20 | ≥25 |
SiO2 | % | ≤82 | ≤77 | ≤70 | |
Fe2O3 | % | ≤2 | ≤2.5 | ≤3 | |
Bulk Density | g/cm3 | 0.8 | 1.0 | 1.3 | |
Apparent Porosity | % | ≤75 | ≤65 | ≤55 | |
Refractoriness | ℃ | ≥1680 | ≥1690 | ≥1700 | |
Cold Crushing Strength | MPa | ≥8 | ≥10 | ≥15 | |
Permanent Linear Change | % | ≤2% | |||
1250℃ | 1350℃ | 1400℃ | |||
Thermal Conductivity (350±25℃) | w/m.k | ≤0.6 | ≤0.5 | ≤0.35 |